70 DENIER NYLON TAFFETA

Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 1.9 Ounces Square Yard 64 Grams Square Meter
Total Weight
5041 5.0 Ounces Square Yard 170 Grams Square Meter
Tongue Tear
5134 1.5 Warp
1.0 Fill (Pounds) 7.0 Warp
4.0 Weft (Newtons)
Tensile Strength
5102 75 Warp
50 Fill (Pounds Inch) 328 Warp
219 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 45 Pounds Inch Warp 197 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 15 Pounds Inch Warp 66 Newtons 25 mm Warp
Hydrostatic High Pressure
Mil-C-83489 4.4.1 100 Pounds Square Inch 689 kPa

Roll your mouse over the sample to see color code.
Applications: Helium Parade Balloons, AirshipAerostat Balloon Ballonets, Remote Controlled Indoor Airships, Parachute Cloth
Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 1.1 Ounces Square Yard 37 Grams Square Meter
Total Weight
5041 3.0 Ounces Square Yard 102 Grams Square Meter
Tongue Tear
5134 1.0 Warp
1.0 Fill (Pounds) 4 Warp
4 Weft (Newtons)
Tensile Strength
5102 40 Warp
35 Fill (Pounds Inch) 175 Warp
153 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 10 Pounds Inch Warp 44 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 5 Pounds Inch Warp 22 Newtons 25 mm Warp
Hydrostatic High Pressure
5512 80 Pounds Square Inch 552 kPa
Air Retention
(Film Side Only)
Mil-C-83489 4.4.2 Pass 3 PSI No Leaks 5 Minutes Pass 21 kPa No Leaks 5 Minutes
Low Temperature
Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40F for 4 Hours No Cracking, Flaking, or Separation at -40C for 4 Hours
Blocking
(Film to Film)
5872 No Blocking at 180F for 30 Minutes No Blocking at 82C for 30 Minutes

210 DENIER NYLON PLAIN

Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 4.3 Ounces Square Yard 146 Grams Square Meter
Total Weight
5041 7.0 Ounces Square Yard 237 Grams Square Meter
Tongue Tear
5134 8 Warp
14 Fill (Pounds) 36 Warp
62 Weft (Newtons)
Tensile Strength
5102 300 Warp
300 Fill (Pounds Inch) 1313 Warp
1313 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 75 Pounds Inch Warp 328 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 20 Pounds Inch Warp 88 Newtons 25 mm Warp
Hydrostatic High Pressure
Mil-C-83489 4.4.1 500 Pounds Square Inch 3447 kPa
Air Retention
(Film Side Only)
Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes
Low Temperature
Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40 Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40 Celsius for 4 Hours
Blocking (Film to Film)
5872 No Blocking at 180F for 30 Minutes No Blocking at 82C for 30 Minutes

Roll your mouse over the sample to see color code.
Applications: Hospital Air Beds, Hospital Patient Transfer Devices, Gel Filled Wheelchair Seat Cushions, Helium Parade Balloons

70 X 100 DENIER NYLON TWILL

Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 2.8 Ounces Square Yard 95 Grams Square Meter
Total Weight
5041 5.8 Ounces Square Yard 195 Grams Square Meter
Tongue Tear
5134 3.0 Warp
2.0 Fill (Pounds) 13 Warp
9 Weft (Newtons)
Tensile Strength
5102 100 Warp
80 Fill (Pounds Inch) 438 Warp
385 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 50 Pounds Inch Warp 219 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 30 Pounds Inch Warp 131 Newtons 25 mm Warp
Hydrostatic High Pressure
Mil-C-83489 4.4.1 230 Pounds Square Inch 1586 kPa
Air Retention
(Film Side Only)
Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes
Low Temperature
Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40 Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40 Celsius for 4 Hours
Blocking (Film to Film)
5872 No Blocking at 180F for 30 Minutes No Blocking at 82C for 30 Minutes

Roll your mouse over the sample to see color code.
Applications: TSO Life Raft Valises, Aviation Rafts, Sonar Buoys, Diving Dry Suits, Hot Water Transfer Bladders, Avalanche Survival Balloons, Military Life Jackets, Signal Buoys, Underground Liners, White Water Rafts, Inflatable Shelter Supports.

210 DENIER NYLON HIGHCOUNT

Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 3.9 Ounces Square Yard 132 Grams Square Meter
Total Weight
5041 8.5 Ounces Square Yard 288 Grams Square Meter
Tongue Tear
5134 9 Warp
7 Fill (Pounds) 40 Warp
31 Weft (Newtons)
Tensile Strength
5102 280 Warp
225 Fill (Pounds Inch) 1226 Warp
985 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 80 Pounds Inch Warp 985 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 45 Pounds Inch Warp 197 Newtons 25 mm Warp
Hydrostatic High Pressure
Mil-C-83489 4.4.1 500 Pounds Square Inch 3447 kPa
Air Retention
(Film Side Only)
Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes
Low Temperature
Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40 Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40 Celsius for 4 Hours
Blocking (Film to Film)
5872 No Blocking at 180F for 30 Minutes No Blocking at 82C for 30 Minutes

200 DENIER NYLON OXFORD

Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 3.1 Ounces Square Yard 105 Grams Square Meter
Total Weight
5041 6.8 Ounces Square Yard 231 Grams Square Meter
Tongue Tear
5134 4 Warp
3 Fill (Pounds) 18 Warp
13 Weft (Newtons)
Tensile Strength
5102 130 Warp
100 Fill (Pounds Inch) 569 Warp
438 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 65 Pounds Inch Warp 285 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 40 Pounds Inch Warp 175 Newtons 25 mm Warp
Hydrostatic High Pressure
Mil-C-83489 4.4.1 275 Pounds Square Inch 1896 kPa
Air Retention
(Film Side Only)
Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes
Low Temperature
Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40 Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40 Celsius for 4 Hours
Blocking (Film to Film)
5872 No Blocking at 180F for 30 Minutes No Blocking at 82C for 30 Minutes

200 DENIER DIAMOND RIPSTOP

Test Reference
Federal Std. 191A
Mil-C-83489 Typical Result
(Standard Units) Typical Result
(International Units)
Base Fabric Weight
5041 3.1 Ounces Square Yard 105 Grams Square Meter
Total Weight
5041 6.8 Ounces Square Yard 231 Grams Square Meter
Tongue Tear
5134 5 Warp
4 Fill (Pounds) 22 Warp
18 Weft (Newtons)
Tensile Strength
5102 130 Warp
100 Fill (Pounds Inch) 569 Warp
438 Weft (Newtons 25 mm)
Breakaway Adhesion
(RF Weld) Film to Film
Mil-C-83489 4.4.1 65 Pounds Inch Warp 285 Newtons 25 mm Warp
Strip Adhesion
(Heat Sealed) Film to Film
5970 40 Pounds Inch Warp 175 Newtons 25 mm Warp
Hydrostatic High Pressure
Mil-C-83489 4.4.1 275 Pounds Square Inch 1896 kPa
Air Retention
(Film Side Only)
Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes
Low Temperature
Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40 Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40 Celsius for 4 Hours
Blocking (Film to Film)
5872 No Blocking at 180F for 30 Minutes No Blocking at 82C for 30 Minutes