Lamcotec

• Series30 DENIER NYLON RIPSTOP

Roll your mouse over the sample to see color code. Applications: Helium Parade Balloons, AirshipAerostat Balloon Ballonets, Remote Controlled Indoor Airships, Parachute Cloth Test Reference Federal Std. 191A Mil-C-83489 Typical Result (Standard Units) Typical Result (International Units) Base Fabric Weight 5041 1.1 Ounces Square Yard 37 Grams Square Meter Total Weight 5041 3.0 Ounces Square Yard 102 Grams Square Meter Tongue Tear 5134 1.0 Warp 1.0 Fill (Pounds) 4 Warp 4 Weft (Newtons) Tensile Strength 5102 40 Warp 35 Fill (Pounds Inch) 175 Warp 153 Weft (Newtons 25 mm) Breakaway Adhesion (RF Weld) Film to Film Mil-C-83489 4.4.1 10 Pounds Inch Warp 44 Newtons 25 mm Warp Strip Adhesion (Heat Sealed) Film to Film 5970 5 Pounds Inch Warp 22 Newtons 25 mm Warp Hydrostatic High Pressure 5512 80 Pounds Square Inch 552 kPa Air Retention (Film Side Only) Mil-C-83489 4.4.2 Pass 3 PSI No Leaks 5 Minutes Pass 21 kPa No Leaks 5 Minutes Low Temperature Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40°F for 4 Hours No Cracking, Flaking, or Separation at -40°C for 4 Hours Blocking (Film to Film) 5872 No Blocking at 180°F for 30 Minutes No Blocking at 82°C for 30 Minutes

• Series70 X 100 DENIER NYLON TWILL

Roll your mouse over the sample to see color code. Applications: Hospital Air Beds, Hospital Patient Transfer Devices, Gel Filled Wheelchair Seat Cushions, Helium Parade Balloons 70 X 100 DENIER NYLON TWILL Test Reference Federal Std. 191A Mil-C-83489 Typical Result (Standard Units) Typical Result (International Units) Base Fabric Weight 5041 2.8 Ounces Square Yard 95 Grams Square Meter Total Weight 5041 5.8 Ounces Square Yard 195 Grams Square Meter Tongue Tear 5134 3.0 Warp 2.0 Fill (Pounds) 13 Warp 9 Weft (Newtons) Tensile Strength 5102 100 Warp 80 Fill (Pounds Inch) 438 Warp 385 Weft (Newtons 25 mm) Breakaway Adhesion (RF Weld) Film to Film Mil-C-83489 4.4.1 50 Pounds Inch Warp 219 Newtons 25 mm Warp Strip Adhesion (Heat Sealed) Film to Film 5970 30 Pounds Inch Warp 131 Newtons 25 mm Warp Hydrostatic High Pressure Mil-C-83489 4.4.1 230 Pounds Square Inch 1586 kPa Air Retention (Film Side Only) Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes Low Temperature Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40° Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40° Celsius for 4 Hours Blocking (Film to Film) 5872 No Blocking at 180°F for 30 Minutes No Blocking at 82°C for 30 Minutes

• SeriesDENIER NYLON HIGHCOUNT

Roll your mouse over the sample to see color code. Applications: TSO Life Raft Valises, Aviation Rafts, Sonar Buoys, Diving Dry Suits, Hot Water Transfer Bladders, Avalanche Survival Balloons, Military Life Jackets, Signal Buoys, Underground Liners, White Water Rafts, Inflatable Shelter Supports. 210 DENIER NYLON HIGHCOUNT Test Reference Federal Std. 191A Mil-C-83489 Typical Result (Standard Units) Typical Result (International Units) Base Fabric Weight 5041 3.9 Ounces Square Yard 132 Grams Square Meter Total Weight 5041 8.5 Ounces Square Yard 288 Grams Square Meter Tongue Tear 5134 9 Warp 7 Fill (Pounds) 40 Warp 31 Weft (Newtons) Tensile Strength 5102 280 Warp 225 Fill (Pounds Inch) 1226 Warp 985 Weft (Newtons 25 mm) Breakaway Adhesion (RF Weld) Film to Film Mil-C-83489 4.4.1 80 Pounds Inch Warp 985 Newtons 25 mm Warp Strip Adhesion (Heat Sealed) Film to Film 5970 45 Pounds Inch Warp 197 Newtons 25 mm Warp Hydrostatic High Pressure Mil-C-83489 4.4.1 500 Pounds Square Inch 3447 kPa Air Retention (Film Side Only) Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes Low Temperature Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40° Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40° Celsius for 4 Hours Blocking (Film to Film) 5872 No Blocking at 180°F for 30 Minutes No Blocking at 82°C for 30 Minutes

• Series70 DENIER NYLON TAFFETA

70 DENIER NYLON TAFFETA Test Reference Federal Std. 191A Mil-C-83489 Typical Result (Standard Units) Typical Result (International Units) Base Fabric Weight 5041 1.9 Ounces Square Yard 64 Grams Square Meter Total Weight 5041 5.0 Ounces Square Yard 170 Grams Square Meter Tongue Tear 5134 1.5 Warp 1.0 Fill (Pounds) 7.0 Warp 4.0 Weft (Newtons) Tensile Strength 5102 75 Warp 50 Fill (Pounds Inch) 328 Warp 219 Weft (Newtons 25 mm) Breakaway Adhesion (RF Weld) Film to Film Mil-C-83489 4.4.1 45 Pounds Inch Warp 197 Newtons 25 mm Warp Strip Adhesion (Heat Sealed) Film to Film 5970 15 Pounds Inch Warp 66 Newtons 25 mm Warp Hydrostatic High Pressure Mil-C-83489 4.4.1 100 Pounds Square Inch 689 kPa

• Series200 DENIER NYLON OXFORD

200 DENIER NYLON OXFORD Test Reference Federal Std. 191A Mil-C-83489 Typical Result (Standard Units) Typical Result (International Units) Base Fabric Weight 5041 3.1 Ounces Square Yard 105 Grams Square Meter Total Weight 5041 6.8 Ounces Square Yard 231 Grams Square Meter Tongue Tear 5134 4 Warp 3 Fill (Pounds) 18 Warp 13 Weft (Newtons) Tensile Strength 5102 130 Warp 100 Fill (Pounds Inch) 569 Warp 438 Weft (Newtons 25 mm) Breakaway Adhesion (RF Weld) Film to Film Mil-C-83489 4.4.1 65 Pounds Inch Warp 285 Newtons 25 mm Warp Strip Adhesion (Heat Sealed) Film to Film 5970 40 Pounds Inch Warp 175 Newtons 25 mm Warp Hydrostatic High Pressure Mil-C-83489 4.4.1 275 Pounds Square Inch 1896 kPa Air Retention (Film Side Only) Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes Low Temperature Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40° Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40° Celsius for 4 Hours Blocking (Film to Film) 5872 No Blocking at 180°F for 30 Minutes No Blocking at 82°C for 30 Minutes

• Series200 DENIER DIAMOND RIPSTOP

200 DENIER DIAMOND RIPSTOP Test Reference Federal Std. 191A Mil-C-83489 Typical Result (Standard Units) Typical Result (International Units) Base Fabric Weight 5041 3.1 Ounces Square Yard 105 Grams Square Meter Total Weight 5041 6.8 Ounces Square Yard 231 Grams Square Meter Tongue Tear 5134 5 Warp 4 Fill (Pounds) 22 Warp 18 Weft (Newtons) Tensile Strength 5102 130 Warp 100 Fill (Pounds Inch) 569 Warp 438 Weft (Newtons 25 mm) Breakaway Adhesion (RF Weld) Film to Film Mil-C-83489 4.4.1 65 Pounds Inch Warp 285 Newtons 25 mm Warp Strip Adhesion (Heat Sealed) Film to Film 5970 40 Pounds Inch Warp 175 Newtons 25 mm Warp Hydrostatic High Pressure Mil-C-83489 4.4.1 275 Pounds Square Inch 1896 kPa Air Retention (Film Side Only) Mil-C-83489 4.4.2 Pass 10 PSI No Leaks 5 Minutes Pass 69 kPa No Leaks 5 Minutes Low Temperature Mil-C-83489 4.4.3 No Cracking, Flaking, or Separation at -40° Fahrenheit for 4 Hours No Cracking, Flaking, or Separation at -40° Celsius for 4 Hours Blocking (Film to Film) 5872 No Blocking at 180°F for 30 Minutes No Blocking at 82°C for 30 Minutes